Technical implementation method of imported gaskets

Classification:


【Summary description】The imported gasket involves the improvement of sealing materials for engines. A gasket plate is disclosed, and its manufacturing technology is also disclosed, belonging to the technical field of asbestos sealing materials. Now let's learn about the technical implementation method of imported gaskets!

The imported gasket involves the improvement of sealing materials for engines. A gasket plate is disclosed, and its manufacturing technology is also disclosed, belonging to the technical field of asbestos sealing materials. Now let's learn about the technical implementation method of imported gaskets!

 

network

 

  进口衬垫技术实现方式:

  目前,小型发动机密封板的原材料主要由石棉纤维、橡胶等制成,由于其材料的限制,由于空气拉伸强度低,产品存在以下缺陷,具有一定的腐蚀性,影响了发动机的质量; 垫圈板在拆装过程中有粘缸现象; 发动机泄漏严重。

  进口衬垫用碾压法将含有氯离子石棉碾压3~5圈,制成石棉绒,首次加入总量1/5的苯溶剂搅拌100分钟,然后加入总量3/5的苯溶剂搅拌90分钟; 搅拌后的材料用张辊压制成形,将上述橡胶混炼成薄片; 将处理后的石棉、纤维、橡胶片及其他材料,工艺条件压力16Mpa、145~150、时间干燥5~10分钟、5~8次压制,将100~110、6~8分钟/片半成品放置在硫化机上以规定的压力、温度硫化。

  进口衬垫是采用含氯离子低石棉纤维和聚氨酯提高了产品的耐腐蚀性,从根本上解决了发动机的泄漏现象,添加石蜡改善了产品的粘性,增加了产品的空气拉伸强度等物性指标。

  进口衬垫用碾压法将含有氯离子石棉65kg碾压3次,将处理后石棉纤维、橡胶片和硫酸钡8kg、聚氨酯清漆2kg、石蜡1.5kg、硫0.1kg、氧化锌0.6kg、促进剂-M0.3、铝粉3、氢钙1混合后,总量1/搅拌后的材料用拉伸机辊压成形,放在硫化机上,制成石棉绒,混炼异戊二烯橡胶8kg、丁腈橡胶10kg后,成形为薄片; 在压力16Mpa、145~150、干燥5~10分钟,在5~8的条件下硫化,得到本发明产品。

  进口衬垫由以下物质以重量份数比制造异戊二烯橡胶5~8、丁腈橡胶10~18、石棉60~75、苯65~98、硫酸钡8~12、聚氨酯清漆1~3、石蜡1~2、硫0.1~0.4

  进口衬垫包括:将处理后的石棉、纤维、橡胶片及其他材料加入总量1/5的苯溶剂搅拌100分钟,用碾压法将按以下步骤完成的含氯离子石棉碾压3~5圈制成石棉绒,半成品放在硫化机上硫化。 硫化条件为16Mpa压力、145~150、干燥5~10分钟,压迫5~8.将上述橡胶磨细制成薄片; 然后加入总量3/5的苯溶剂搅拌90分钟; 搅拌后的材料用拉伸机辊轧成形。

  进口衬垫是按重量份数比制备异戊二烯橡胶、丁腈橡胶、石棉、苯、硫酸钡、聚氨酯清漆、石蜡、硫、氧化锌、促进剂-M、铝粉、氢钙的产品,用碾压法将含有氯离子的石棉碾压5圈,制成石棉绒,搅拌后的材料用拉伸机辊轧成型,半成品放置在硫化机上,在规定的压力、温度下硫化。 将上述橡胶混炼成薄片; 处理后的石棉、纤维、橡胶片及其他材料,加入总量1/5的苯溶剂搅拌后,添加石蜡改善了产品粘性,增加了产品的空气拉伸强度等物性指标,加入总量3/5的苯溶剂搅拌; 采用含氯低石棉纤维和聚氨酯提高了产品的耐腐蚀性,从根本上解决了发动机的泄漏现象。

  以上介绍的就是进口衬垫的技术实现方式,如想了解更多,可随时联系我们!